ASTM B610-19
Standard Test Method for Measuring Dimensional Changes Associated with Processing Metal Powders Intended for Die Compaction
- Standard No.
- ASTM B610-19
- Release Date
- 2019
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM B610-23
- Latest
- ASTM B610-23
- Scope
- 1.1 This standard covers a test method that may be used to measure the sum of the changes in dimensions that occur when a metal powder is first compacted into a test specimen and then sintered. 1.2 The dimensional change is determined by a quantitative laboratory procedure in which the arithmetic difference between the dimensions of a die cavity and the dimensions of a sintered test specimen produced from that die is calculated and expressed as a percent growth or shrinkage. 1.3 With the exception of the values for density and the mass used to determine density, for which the use of the gram per cubic centimetre (g/cm3 ) and gram (g) units is the longstanding industry practice, the values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM B610-19 Referenced Document
- ASTM B215 Standard Practices for Sampling Finished Lots of Metal Powders
- ASTM B243 Standard Terminology of Powder Metallurgy*， 2023-05-01 Update
- ASTM B925 Standard Practices for Production and Preparation of Powder Metallurgy (PM) Test Specimens*， 2022-03-01 Update
- ASTM B962 Standard Test Methods for Density of Compacted or Sintered Powder Metallurgy (PM) Products Using Archimedes’ Principle*， 2023-09-01 Update
ASTM B610-19 history
- 2023 ASTM B610-23 Standard Test Method for Measuring Dimensional Changes Associated with Processing Metal Powders Intended for Die Compaction
- 2019 ASTM B610-19 Standard Test Method for Measuring Dimensional Changes Associated with Processing Metal Powders Intended for Die Compaction
- 2013 ASTM B610-13 Standard Test Method for Measuring Dimensional Changes Associated with Processing Metal Powders
- 2008 ASTM B610-08 Standard Test Method for Measuring Dimensional Changes Associated with Processing Metal Powders
- 2000 ASTM B610-00e1 Standard Test Method for Measuring Dimensional Changes of Metal Powder Specimens