SAE ARP1631A-2018
Manufacturing Sequence for Fabrication of High-Strength Steel Parts 300M or 4340 Modified Low-Alloy Steels 270,000 psi (1860 MPa) Tensile Strength and Higher
- Standard No.
- SAE ARP1631A-2018
- Release Date
- 2018
- Published By
- Society of Automotive Engineers (SAE)
- Latest
- SAE ARP1631A-2018
- Scope
- This document establishes the requirements for the sequencing of processes relating to parts fabricated from 300M or 4340 modified steel heat treated to, or to be heat treated to, 270,000 psi (1860 MPa) minimum ultimate tensile strength (UTS) and higher.
SAE ARP1631A-2018 history
- 2018 SAE ARP1631A-2018 Manufacturing Sequence for Fabrication of High-Strength Steel Parts 300M or 4340 Modified Low-Alloy Steels 270,000 psi (1860 MPa) Tensile Strength and Higher
- 2007 SAE ARP1631A-2007 Manufacturing Sequence for Fabrication of High-Strength Steel Parts 300M or 4340 Modified Low-Alloy Steels 270,000 psi (1860 MPa) Tensile Strength and Higher
- 1984 SAE ARP1631-1984 Manufacturing Sequence for Fabrication of High- Strength Steel Parts 300M or 4340 Modified Low-Alloy Steels 270@000 psi (1860 MPa) Tensile Strength and Higher