1.1 This specification covers requirements of wrought 35cobalt-35nickel-20chromium-10molybdenum alloy (UNS R30035) in the form of bar and wire, used for the manufacture of surgical implants. This alloy depends on combinations of work strengthening and aging to attain a variety of combinations of strength and ductility.
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other and values from the two systems shall not be combined.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM F562-22 Referenced Document
ASTM A751 Standard Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products
ASTM E112 Standard Test Methods for Determining Average Grain Size
ASTM E29 Standard Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
ASTM E354 Standard Test Methods for Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron, Nickel, and Cobalt Alloys
ASTM E8/E8M Standard Test Methods for Tension Testing of Metallic Materials*, 2024-01-01 Update
ASTM F981 Standard Practice for Assessment of Compatibility of Biomaterials for Surgical Implants with Respect to Effect of Materials on Muscle and Bone
IEEE/ASTM SI 10 American National Standard for Metric Practice