1.1 This test method gives an indication of the oxidation resistance of raw natural rubber at a specified temperature. This resistance is indicated by the Plasticity Retention Index (PRI), a ratio expressed as a percentage of the aged plasticity to the original plasticity determined by means of a parallel plate plastometer. A low PRI value indicates a poor resistance to oxidation.
1.2 The values stated in SI units are to be regarded as the standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D3194-17(2022) Referenced Document
ASTM D1485 Standard Test Methods for Rubber from Natural Sources-Sampling and Sample Preparation
ASTM D3182 Standard Practice for Rubber-Materials, Equipment, and Procedures for Mixing Standard Compounds and Preparing Standard Vulcanized Sheets
ASTM E145 Standard Specification for Gravity-Convection And Forced-Ventilation Ovens
ASTM D3194-17(2022) history
2022ASTM D3194-17(2022) Standard Test Method for Rubber From Natural Sources—Plasticity Retention Index (PRI)
2017ASTM D3194-17 Standard Test Method for Rubber From Natural Sources—Plasticity Retention Index (PRI)
2004ASTM D3194-04(2009) Standard Test Method for Rubber From Natural Sources-Plasticity Retention Index (PRI)
2004ASTM D3194-04 Standard Test Method for Rubber From Natural Sources-Plasticity Retention Index (PRI)
1999ASTM D3194-99 Standard Test Method for Rubber From Natural Sources-Plasticity Retention Index (PRI)