Nickel Alloy@ Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 Degrees F (977 to 1077 Degrees C) Solidus-Liquidus Range (UNS N99600)

Standard No.

SAE AMS4775F-1994

Release Date

1994

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS4775G-1995

Latest

SAE AMS4775L-2023

Scope

Form: This specification covers a nickel alloy in the form of wire@ rod@ strip@ and powder and a viscous mixture (paste) of powder in a suitable binder. Application: This filler metal has been used typically for joining corrosion and heat resistant steels and alloys corrosion and oxidation on resistant joints with good strength at elevated temperatures. Also may be used as a corrosion and oxidation resistant hard coating.

SAE AMS4775F-1994 history

• 2023 SAE AMS4775L-2023 Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus
• 2018 SAE AMS4775K-2018 Nickel Alloy@ Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 °F (977 °C) Solidus to 1970 °F (1077 °C) Liquidus (UNS N99600)
• 2010 SAE AMS4775J-2010 Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 Degrees F (977 to 1077 Degrees C) Solidus-Liquidus Range (UNS N99600)
• 2005 SAE AMS4775H-2005 Nickel Alloy, Brazing Filler Metal 73Ni 0.75C 4.5Si 14Cr 3.1B 4.5Fe, 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range
• 2000 SAE AMS4775G-2000 Nickel Alloy, Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range
• 1995 SAE AMS4775G-1995 Nickel Alloy, Brazing Filler Metal 73Ni 0.75C 4.5Si 14Cr 3.1B 4.5Fe, 1790 to 1970°F (977 to 1077°C) Solidus-Liquidus Range (Reaffirmed: 01 Aug 2000)
• 1994 SAE AMS4775F-1994 Nickel Alloy@ Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 Degrees F (977 to 1077 Degrees C) Solidus-Liquidus Range (UNS N99600)
• 1992 SAE AMS4775E-1992 Nickel Alloy Brazing Filler Metal 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790 to 1970 Degrees F (977 to 1077 Degrees C) Solidus-Liquidus Range (UNS N99600)
• 1988 SAE AMS4775D-1988 Brazing Filler Metal@ Nickel Alloy 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790° - 1970°F (977° - 1077°C) Solidus-Liquidus Range (UNS N99600)
• 1981 SAE AMS4775C-1981 Brazing Filler Metal@ Nickel 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790° - 1970° F (975° to 1075°C) Solidus-Liquidus Range
• 1978 SAE AMS4775B-1978 Brazing Filler Metal@ Nickel 73Ni - 0.75C - 4.5Si - 14Cr - 3.1B - 4.5Fe 1790° - 1970°F (975° - 1075°C) Solidus-Liquidus Range
• 1956 SAE AMS4775A-1956 Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B
• 1952 SAE AMS4775-1952 Brazing Alloy Nickel Base - 4Si - 16.5Cr - 4Fe - 3.8B - 1C