SAE AMS5744C-2011
STEEL BARS AND FORGINGS, CORROSION AND MODERATE HEAT RESISTANT 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated, 170,000 psi (1170 MPa) Tensile Strength
Home
SAE AMS5744C-2011
Standard No.
SAE AMS5744C-2011
Release Date
2011
Published By
Society of Automotive Engineers (SAE)
Status
Be replaced
Replace By
SAE AMS5744E-2013
Latest
SAE AMS5744F-2019
Scope
This specification covers a corrosion and moderate heat resistant steel in the form of bars, forgings, and forging stock.
SAE AMS5744C-2011 history
2019
SAE AMS5744F-2019
Steel, Corrosion and Heat-Resistant, Bars and Forgings 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Consumable Electrode Remelted Heat Treated, 170 ksi (1172 MPa) Tensile Strength
2013
SAE AMS5744E-2013
Steel, Corrosion and Heat-Resistant, Bars and Forgings 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated, 170 ksi (1172 MPa) Tensile Strength
2011
SAE AMS5744C-2011
STEEL BARS AND FORGINGS, CORROSION AND MODERATE HEAT RESISTANT 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated, 170,000 psi (1170 MPa) Tensile Strength
2003
SAE AMS5744E-2003
Steel, Corrosion and Heat-Resistant, Bars and Forgings 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated, 170 ksi (1172 MPa) Tensile Strength UNS S35500
2000
SAE AMS5744D-2000
Steel, Corrosion and Heat Resistant, Bars and Forgings 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated, 170 ksi (1172 MPa) Tensile Strength
1993
SAE AMS5744D-1993
Steel@ Corrosion and Heat Resistant@ Bars and Forgings 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated@ 170 ksi (1172 MPa) Tensile Strength (UNS S35500)
1981
SAE AMS5744B-1981
STEEL BARS AND FORGINGS, CORROSION AND MODERATE HEAT RESISTANT 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated, 170,000 psi (1172 MPa) Tensile Strength
1973
SAE AMS5744A-1973
STEEL BARS AND FORGINGS, CORROSION AND MODERATE HEAT RESISTANT 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated, 170,000 psi (1172 MPa) Tensile Strength
1965
SAE AMS5744-1965
STEEL BARS AND FORGINGS, CORROSION AND MODERATE HEAT RESISTANT 15.5Cr - 4.5Ni - 2.9Mo - 0.10N Heat Treated (170,000 psi Tensile)
Copyright ©2024 All Rights Reserved