1.1 This specification and test methods cover the mechanical characterization of plates and screws for orthopedic internal fixation. Covered devices are fabricated from one or more hydrolytically degradable polymer (from this point on referred to as “absorbable”) resins or resin composites.
1.2 This specification establishes a common terminology to describe the size and other physical characteristics of absorbable implants and performance definitions related to the performance of absorbable devices.
1.3 This specification establishes standard test methods to consistently measure performance-related mechanical characteristics of absorbable devices when tested under defined conditions of pretreatment, temperature, humidity, and testing machine speed.
1.4 This specification may not be appropriate for all absorbable devices, especially those that possess limited hydrolytic susceptibility and degrade in vivo primarily through enzymatic action. The user is cautioned to consider the appropriateness of the standard in view of the particular absorbable device and its potential application.
1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health and environmental practices and determine the applicability of regulatory limitations prior to use.
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM F2502-17 Referenced Document
ASTM D790 Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials*, 2024-04-21 Update
ASTM E122 Standard Practice for Calculating Sample Size to Estimate, With a Specified Tolerable Error, the Average for Characteristic of a Lot or Process
ASTM E1823 Standard Terminology Relating to Fatigue and Fracture Testing
ASTM E4 Standard Practices for Force Verification of Testing Machines
ASTM E6 Standard Terminology Relating to Methods of Mechanical Testing
ASTM F1088 Standard Specification for Beta-Tricalcium Phosphate for Surgical Implantation
ASTM F116 Standard Specification for Medical Screwdriver Bits*, 2021-02-01 Update
ASTM F1185 Standard Specification for Composition of Ceramic Hydroxylapatite for Surgical Implants
ASTM F1635 Standard Test Method for In Vitro Degradation Testing of Poly (L-lactic Acid) Resin and Fabricated Form for Surgical Implants
ASTM F1839 Standard Specification for Rigid Polyurethane Foam for Use as a Standard Material for Testing Orthopaedic Devices and Instruments
ASTM F1925 Standard Specification for Virgin Poly(L-Lactic Acid) Resin for Surgical Implants
ASTM F2313 Standard Specification for Poly(glycolide) and Poly(glycolide-co-lactide) Resins for Surgical Implants with Mole Fractions Greater Than or Equal to 70 % Glycolide*, 2018-12-15 Update
ASTM F2503 Standard Practice for Marking Medical Devices and Other Items for Safety in the Magnetic Resonance Environment*, 2023-04-01 Update
ASTM F2579 Standard Specification for Amorphous Poly(lactide) and Poly(lactide-co-glycolide) Resins for Surgical Implants*, 2018-12-15 Update
ASTM F2902 Standard Guide for Assessment of Absorbable Polymeric Implants
ASTM F3160 Standard Guide for Metallurgical Characterization of Absorbable Metallic Materials for Medical Implants*, 2021-02-01 Update
ASTM F382 Standard Specification and Test Method for Metallic Bone Plates
ASTM F543 Standard Specification and Test Methods for Metallic Medical Bone Screws
ASTM F565 Standard Practice for Care and Handling of Orthopedic Implants and Instruments*, 2021-04-01 Update
ISO 13781 Implants for surgery - Homopolymers, copolymers and blends on poly(lactide) - In vitro degradation testing
ISO 14630 Non-active surgical implants - General requirements
ISO 15814 Implants for surgery - Copolymers and blends based on polylactide - In vitro degradation testing
ASTM F2502-17 history
2017ASTM F2502-17 Standard Specification and Test Methods for Absorbable Plates and Screws for Internal Fixation Implants
2011ASTM F2502-11 Standard Specification and Test Methods for Bioabsorbable Plates and Screws for Internal Fixation Implants
2005ASTM F2502-05(2009)e1 Standard Specification and Test Methods for Bioabsorbable Plates and Screws for Internal Fixation Implants
2005ASTM F2502-05 Standard Specification and Test Methods for Bioabsorbable Plates and Screws for Internal Fixation Implants