ASTM A913/A913M-19
Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)

Standard No.

ASTM A913/A913M-19

Release Date

2019

Published By

American Society for Testing and Materials (ASTM)

Latest

ASTM A913/A913M-19

Scope

1.1 This specification covers high-strength low-alloy structural steel shapes in Grades 50 [345], 60 [415], 65 [450], 70 [485], and 80 [550], produced by the quenching and selftempering process (QST). The shapes are intended for riveted, bolted or welded construction of bridges, buildings and other structures. 1.2 The QST process consists of in line heat treatment and cooling rate controls which result in mechanical properties in the finished condition that are equivalent to those attained using heat treating processes which entail reheating after rolling. A description of the QST process is given in Appendix X1. 1.3 Due to the inherent characteristics of the QST process, Grade 50 [345], 60 [415], 65 [450], and 70 [485] shapes shall not be formed nor post weld heat treated at temperatures exceeding 1100°F [595°C] and Grade 80 [550] shapes shall not be formed nor post weld heat treated at temperatures exceeding 1000°F [540°C]. 1.4 When the steel is to be welded, it is presupposed that a welding procedure suitable for the grade of steel and intended use or service will be utilized. See Appendix X3 of Specification A6/A6M for information on weldability. 1.5 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification. 1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM A913/A913M-19 Referenced Document

• ASTM A6/A6M Standard Specification for General Requirements for Rolled Structural Steel Bars, Plates, Shapes, and Sheet Piling*， 2024-03-01 Update
• ASTM A673/A673M Standard Specification for Sampling Procedure for Impact Testing of Structural Steel
• ASTM A898/A898M Standard Specification for Straight Beam Ultrasonic Examination of Rolled Steel Structural Shapes

ASTM A913/A913M-19 history

• 2019 ASTM A913/A913M-19 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)
• 2015 ASTM A913/A913M-15 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)
• 2014 ASTM A913/A913M-14a Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process 40;QST41;
• 2014 ASTM A913/A913M-14 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process 40;QST41;
• 2011 ASTM A913/A913M-11 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process
• 2007 ASTM A913/A913M-07 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)
• 2004 ASTM A913/A913M-04 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)
• 2003 ASTM A913/A913M-03 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)
• 2001 ASTM A913/A913M-01 Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)
• 2000 ASTM A913/A913M-00a Standard Specification for High-Strength Low-Alloy Steel Shapes of Structural Quality, Produced by Quenching and Self-Tempering Process (QST)