1.1 This test method covers the determination of the percent weight loss of cured solventless electrical varnishes when exposed to elevated temperatures for prescribed periods of time.
1.2 Results of this test method are based on 6-mm (1⁄4-in.) thick specimens and will not be applicable to specimens appreciably thinner or thicker than 6 mm.
1.3 The values stated in SI units are to be regarded as the standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. NOTE 1—This standard resembles IEC 60216–2 “Guide for the determination of thermal endurance properties of electrical insulating materials. Part 2: Choice of test criteria” in a number of ways, but is not consistently similar throughout. The data obtained using either standard will possibly be technically equivalent.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM D3377-04(2018) Referenced Document
ASTM D1711 Standard Terminology Relating to Electrical Insulation
ASTM D5423 Standard Specification for Forced-Convection Laboratory Ovens for Evaluation of Electrical Insulation
ASTM D3377-04(2018) history
2018ASTM D3377-04(2018) Standard Test Method for Weight Loss of Solventless Varnishes
2004ASTM D3377-04(2013) Standard Test Method for Weight Loss of Solventless Varnishes
2004ASTM D3377-04(2009) Standard Test Method for Weight Loss of Solventless Varnishes
2004ASTM D3377-04 Standard Test Method for Weight Loss of Solventless Varnishes
2000ASTM D3377-00 Standard Test Method for Weight Loss of Solventless Varnishes
1996ASTM D3377-96 Standard Test Method for Weight Loss of Solventless Varnishes