SAE AMS4108-1975
ALUMINUM ALLOY HAND FORGINGS 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T73652) Solution Heat Treated, Compression Stress-Relieved, and Precipitation Heat Treated
Home
SAE AMS4108-1975
Standard No.
SAE AMS4108-1975
Release Date
1975
Published By
Society of Automotive Engineers (SAE)
Status
Be replaced
Replace By
SAE AMS4108A-1977
Latest
SAE AMS4108F-2015
Scope
This specification covers an aluminum alloy in the form of high-strength hand forgings with thicknesses to 8 in. (203 mm) and of forging stock.
SAE AMS4108-1975 history
2015
SAE AMS4108F-2015
Aluminum Alloy, Hand Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) Solution Heat Treated, Compression Stress-Relieved, and Overaged
2011
SAE AMS4108D-2011
ALUMINUM ALLOY HAND FORGINGS 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) (formerly -T73652) Solution Heat Treated, Compression Stress-Relieved, and Overaged
2003
SAE AMS4108F-2003
Aluminum Alloy@ Hand Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) Solution Heat Treated@ Compression Stress-Relieved@ and Overaged (UNS A97050)
1996
SAE AMS4108E-1996
Aluminum Alloy@ Hand Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) Solution Heat Treated@ Compression Stress-Relieved@ and Overaged (UNS A97050)
1987
SAE AMS4108C-1987
Aluminum Alloy Hand Forgings 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T7452) (formerly -T73652) Solution Heat Treated@ Compression Stress-Relieved@ and Overaged (UNS A97050)
1984
SAE AMS4108B-1984
ALUMINUM ALLOY HAND FORGINGS 6.2Zn - 2.3Cu - 2.2Mg - 0.12zr (7050-T7452) (formerly -T73652) Solution Heat Treated, Compression Stress-Relieved, and Overaged
1977
SAE AMS4108A-1977
ALUMINUM ALLOY HAND FORGINGS 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T73652) Solution Heat Treated, Compression Stress-Relieved, and Precipitation Heat Treated
1975
SAE AMS4108-1975
ALUMINUM ALLOY HAND FORGINGS 6.2Zn - 2.3Cu - 2.2Mg - 0.12Zr (7050-T73652) Solution Heat Treated, Compression Stress-Relieved, and Precipitation Heat Treated
Copyright ©2024 All Rights Reserved