ASTM A710/A710M-19
Standard Specification for Precipitation–Strengthened Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium (Niobium) Alloy Structural Steel Plates

Standard No.

ASTM A710/A710M-19

Release Date

2019

Published By

American Society for Testing and Materials (ASTM)

Latest

ASTM A710/A710M-19

Scope

1.1 This specification covers low-carbon precipitation — strengthened nickel copper chromium molybdenum columbium (niobium) alloy steel plates for general applications. The alloys in this specification are strengthened by precipitation in various temperature ranges. Precipitation strengthening can occur upon air cooling after hot rolling, during normalizing, and by another heat treatment. These grades are not intended for use in applications above 900°F [480°C]. 1.2 Two grades, each with three classes, are provided as follows: Grade and Class Condition Grade A, Class 1 as-rolled and precipitation heat treated Grade A, Class 2 normalized and precipitation heat treated Grade A, Class 3 quenched and precipitation heat treated Grade B, Class 1 as-rolled Grade B, Class 2 normalized Grade B, Class 3 normalized and precipitation heat treated 1.3 Grade A provides minimum yield strength levels ranging from 50 to 85 ksi [345 to 585 MPa], depending on thickness and condition. 1.4 Grade A, Class 1, plates are limited to a maximum thickness of 3⁄4 in. [20 mm]. The maximum thickness of Grade A, Classes 2 and 3, is limited only by the capacity of the composition to meet the specified mechanical property requirements; however, current practice normally limits the maximum thickness to 8 in. [200 mm]. 1.5 Mandatory notch toughness requirements are specified for Grade A, Class 1. 1.6 Grade B provides minimum yield strength levels ranging from 70 to 75 ksi [485 to 515 MPa], depending on thickness and condition. 1.7 Grade B plates are limited to a maximum thickness of 2 in. [50 mm]. 1.8 Mandatory notch toughness requirements are specified for the three classes of Grade B. 1.9 When the steel is to be welded, it is presupposed that a welding procedure suitable for the grade of steel and intended use or service will be utilized. See Appendix X3 of Specification A6/A6M for information on weldability. 1.10 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. 1.11 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ASTM A710/A710M-19 Referenced Document

• ASTM A370 Standard Test Methods and Definitions for Mechanical Testing of Steel Products
• ASTM A6/A6M Standard Specification for General Requirements for Rolled Structural Steel Bars, Plates, Shapes, and Sheet Piling*， 2024-03-01 Update
• ASTM A673/A673M Standard Specification for Sampling Procedure for Impact Testing of Structural Steel

ASTM A710/A710M-19 history

• 2019 ASTM A710/A710M-19 Standard Specification for Precipitation–Strengthened Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium (Niobium) Alloy Structural Steel Plates
• 2002 ASTM A710/A710M-02(2013) Standard Specification for Precipitationndash;Strengthened Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium Alloy Structural Steel Plates
• 2002 ASTM A710/A710M-02(2007) Standard Specification for Precipitation-Strengthened Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium Alloy Structural Steel Plates
• 2002 ASTM A710/A710M-02 Standard Specification for Precipitation-Strengthened Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium Alloy Structural Steel Plates
• 2001 ASTM A710/A710M-01 Standard Specification for Age-Hardening Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium Alloy Structural Steel Plates
• 2000 ASTM A710/A710M-00 Standard Specification for Age-Hardening Low-Carbon Nickel-Copper-Chromium-Molybdenum-Columbium Alloy Structural Steel Plates