1.1 This specification covers wire and rod in the alloys (Note 1) shown in Table 1 and the tempers shown in Table 2 [Table 3] and Table 4 [Table 5], suitable for manufacturing rivets and other similar items by cold-heading operations. NOTE 1—Throughout this specification the use of the term alloy in the general sense includes aluminum as well as aluminum alloy. NOTE 2—For rolled or cold-finished wire and rod, see Specification B211, and for extruded wire and rod, see Specification B221.
1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1M. The equivalent Unified Numbering System alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527.
1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.
1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4.1 The SI units are shown either in brackets or in separate tables.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM B316/B316M-20 Referenced Document
ASTM B211 Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire
ASTM B221 Standard Specification for Aluminum-Alloy Extruded Bars, Rods, Wire, Shapes, and Tubes
ASTM B557 Standard Test Methods of Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products
ASTM B557M Standard Test Methods of Tension Testing Wrought and Cast Aluminum- and Magnesium-Alloy Products [Metric]
ASTM B565 Standard Test Method for Shear Testing of Aluminum and Aluminum-Alloy Rivets and Cold-Heading Wire and Rods
ASTM B660 Standard Practices for Packaging/Packing of Aluminum and Magnesium Products
ASTM B666/B666M Standard Practice for Identification Marking of Aluminum and Magnesium Products
ASTM B918 Standard Practice for Heat Treatment of Wrought Aluminum Alloys*, 2024-04-21 Update
ASTM B985 Standard Practice for Sampling Aluminum Ingots, Billets, Castings and Finished or Semi-Finished Wrought Aluminum Products for Compositional Analysis*, 2024-04-21 Update
ASTM E1004 Standard Practice for Determining Electrical Conductivity Using the Electromagnetic (Eddy-Current) Method
ASTM E1251 Standard Test Method for Optical Emission Spectrometric Analysis of Aluminum and Aluminum Alloys by the Argon Atmosphere, Point-to-Plane, Unipolar Self-Initiating Capacitor Discharge
ASTM E29 Standard Practice for Using Significant Digits in Test Data to Determine Conformance with Specifications
ASTM E3061 Standard Test Method for Analysis of Aluminum and Aluminum Alloys by Inductively Coupled Plasma Atomic Emission Spectrometry (Performance Based Method)*, 2024-04-21 Update
ASTM E527 Standard Practice for Numbering Metals and Alloys (UNS)
ASTM E716 Standard Practices for Sampling Aluminum and Aluminum Alloys for Spectrochemical Analysis
SAE AMS2772 Heat Treatment of Aluminum Alloy Raw Materials (01 1997)
ASTM B316/B316M-20 history
2020ASTM B316/B316M-20 Standard Specification for Aluminum and Aluminum-Alloy Rivet and Cold-Heading Wire and Rods
2015ASTM B316/B316M-15 Standard Specification for Aluminum and Aluminum-Alloy Rivet and Cold-Heading Wire and Rods
2010ASTM B316/B316M-10 Standard Specification for Aluminum and Aluminum-Alloy Rivet and Cold-Heading Wire and Rods
2002ASTM B316/B316M-02 Standard Specification for Aluminum and Aluminum-Alloy Rivet and Cold-Heading Wire and Rods
2000ASTM B316/B316M-00 Standard Specification for Aluminum and Aluminum-Alloy Rivet and Cold-Heading Wire and Rods