Nickel Alloy@ Corrosion and Heat-Resistant@ Round Bars and Wire 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted 1775 Degrees F (968 Degrees C) Solution Treated and Work Strengthened Precipitation Hard

Standard No.

SAE AMS5962A-2003

Release Date

2003

Published By

SAE - SAE International

Status

Be replaced

Replace By

SAE AMS5962A-2022

Latest

SAE AMS5962A-2022

Scope

Form: This specification covers a corrosion and heat resistant work strengthened nickel alloy in the form of bars and wire@ 1? inches (38 mm) and under in nominal diameter (See 8.2). Application: These products have been used typically for parts@ such as fasteners@ requiring a room temperature minimum tensile strength of 220 ksi (1517 MPa) after precipitation heat treatment for use up to 900 ??(482 ?? and having oxidation resistance up to 1800 ??(982 ??@ but usage is not limited to such applications.

SAE AMS5962A-2003 history

• 2022 SAE AMS5962A-2022 Nickel Alloy, Corrosion and Heat-Resistant, Round Bars and Wire 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted 1775 °F (968 °C) Solution Treated and Work Strengthened Precipitation Hardenable
• 2003 SAE AMS5962A-2003 Nickel Alloy@ Corrosion and Heat-Resistant@ Round Bars and Wire 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50Al - 18Fe Consumable Electrode or Vacuum Induction Melted 1775 Degrees F (968 Degrees C) Solution Treated and Work Strengthened Precipitation Hard
• 1997 SAE AMS5962-1997 Nickel Alloy@ Corrosion and Heat Resistant@ Bar and Wire 52.5Ni - 19Cr - 3.0Mo - 5.1Cb - 0.90Ti - 0.50AL - 19Fe Consumable Electrode or Vacuum Induction Melted 1775 Degrees F (968 Degrees C) Solution Treated and Cold Worked Precipitation Hardenable