SAE AMS5740E-2006
Steel@ Corrosion and Moderate Heat Resistant@ Bars@ Forgings@ and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged@ 155@000 psi (1070 MPa) Tensile Strength (UNS S36200)

Standard No.

SAE AMS5740E-2006

Release Date

2006

Published By

SAE - SAE International

Status

Withdraw 2006-05

Latest

SAE AMS5740E-2006

Scope

Form:This specification covers a corrosion and moderate heat resistant steel in the form of bars@ wire@ forgings@ flash welded rings@ and stock for forging or flash welded rings.Application:Primarily for parts requiring corrosion resistance and high strength up to 600??(315??.

SAE AMS5740E-2006 history

• 2006 SAE AMS5740E-2006 Steel@ Corrosion and Moderate Heat Resistant@ Bars@ Forgings@ and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged@ 155@000 psi (1070 MPa) Tensile Strength (UNS S36200)
• 2000 SAE AMS5740D-2000 Steel, Corrosion and Moderate Heat Resistant, Bars, Forgings, and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 155,000 psi (1070 MPa) Tensile Strength
• 1991 SAE AMS5740D-1991 Steel@ Corrosion and Moderate Heat Resistant@ Bars@ Forgings@ and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged@ 155@000 psi (1070 MPa) Tensile Strength (Reaf. Noncur. November 2000; UNS S36200)
• 1989 SAE AMS5740D-1989 (Noncurrent)Steel, Corrosion and Moderate Heat Resistant, Bars, Forgings, and Rings 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 155,000 psi (1070 MPa) Tensile Strength Reaf. Noncur. November 2000; UNS S36200
• 1987 SAE AMS5740C-1987 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 155,000 psi (1070 MPa) Tensile Strength
• 1981 SAE AMS5740B-1981 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Heat Treated and Maraged, 155,000 psi (1069 MPa) Tensile Strength
• 1974 SAE AMS5740A-1974 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Treated and Maraged, 155,000 psi (1069 MPa) Tensile Strength
• 1968 SAE AMS5740-1968 STEEL BARS, FORGINGS, AND RINGS, CORROSION AND MODERATE HEAT RESISTANT 14.5Cr - 6.5Ni - 0.72Ti Solution Treated and Maraged (155,000 psi)