SAE AMS4225A-1984
Aluminum Alloy Castings@ Sand@ Moderate Heat Resistance 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr (203.0p) Solution Heat Treated and Overaged (UNS A02030)
Home
SAE AMS4225A-1984
Standard No.
SAE AMS4225A-1984
Release Date
1984
Published By
SAE - SAE International
Status
Be replaced
2012-12
Replace By
SAE AMS4225B-1991
Latest
SAE AMS4225E-2018
Scope
Form: This specification covers an aluminum alloy in the form of sand castings. Application: Primarily for components requiring moderate strength and good stability up to 600 ??(315?? with resistance to stress-corrosion cracking.
SAE AMS4225A-1984 history
2018
SAE AMS4225E-2018
Aluminum Alloy@ Heat-Resistant@ Castings 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr (203.0-T6) Solution Heat Treated and Precipitation Heat Treated (UNS A02030)
2017
SAE AMS4225D-2017
Aluminum Alloy, Heat-Resistant, Castings 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr (203.0-T6) Solution Heat Treated and Precipitation Heat Treated
2007
SAE AMS4225D-2007
Aluminum Alloy, Heat-Resistant, Castings 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr (203.0-T6) Solution Heat Treated and Precipitation Heat Treated
2007
SAE AMS4225-2007
Aluminum Alloy Castings@ Sand@ Moderate Heat Resistant 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr Solution and Precipitation Heat Treated
1996
SAE AMS4225C-1996
Aluminum Alloy, Heat Resistant, Castings 5.0Cu 1.5Ni 0.25Mn 0.25Sb 0.25Co 0.20Ti 0.20Zr, Solution Heat Treated and Stabilized
1995
SAE AMS4225B-1995
ALUMINUM ALLOY CASTINGS, SAND, HEAT RESISTANT 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr (203.0P) Solution Heat Treated and Stabilized
1991
SAE AMS4225B-1991
Aluminum Alloy Castings@ Sand@ Heat Resistant 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr (203.0P) Solution Heat Treated and Stabilized (UNS A02030)
1984
SAE AMS4225A-1984
Aluminum Alloy Castings@ Sand@ Moderate Heat Resistance 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr (203.0p) Solution Heat Treated and Overaged (UNS A02030)
1968
SAE AMS4225-1968
ALUMINUM ALLOY CASTINGS, SAND, MODERATE HEAT RESISTANT 5.0Cu - 1.5Ni - 0.25Mn - 0.25Sb - 0.25Co - 0.20Ti - 0.20Zr Solution and Precipitation Heat Treated