1.1?This test method covers a procedure for determination of the effective case depth of powder metallurgy (PM) parts. 1.2?A microindentation hardness traverse procedure is described to determine effective case depth. This test method may be used to determine the effective case
ASTM B934-21 Referenced Document
ASTM B243 Standard Terminology of Powder Metallurgy*, 2023-05-01 Update
ASTM B933 Standard Test Method for Microindentation Hardness of Powder Metallurgy (PM) Materials
ASTM E384 Standard Test Method for Microindentation Hardness of Materials
ASTM E691 Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
ASTM B934-21 history
2021ASTM B934-21 Standard Test Method for Effective Case Depth of Ferrous Powder Metallurgy (PM) Parts Using Microindentation Hardness Measurements
2015ASTM B934-15 Standard Test Method for Effective Case Depth of Ferrous Powder Metallurgy (PM) Parts Using Microindentation Hardness Measurements
2010ASTM B934-10 Standard Test Method for Effective Case Depth of Ferrous Powder Metallurgy (P/M) Parts Using Microindentation Hardness Measurements
2004ASTM B934-04a Standard Test Method for Effective Case Depth of Ferrous Powder Metallurgy (P/M) Parts Using Microindentation Hardness Measurements
2004ASTM B934-04 Standard Test Method for Effective Case Depth of Ferrous Powder Metallurgy (P/M) Parts Using Microindentation Hardness Measurements