ASTM A747/A747M-18
Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- Standard No.
- ASTM A747/A747M-18
- Release Date
- 2018
- Published By
- American Society for Testing and Materials (ASTM)
- Status
- Replace By
- ASTM A747/A747M-23
- Latest
- ASTM A747/A747M-23
- Scope
- 1.1 This specification covers iron-chromium-nickel-copper corrosion-resistant steel castings, capable of being strengthened by precipitation hardening heat treatment. 1.2 These castings may be used in services requiring corrosion resistance and high strengths at temperatures up to 600 °F [315 °C]. They may be machined in the solution heat-treated condition and subsequently precipitation hardened to the desired high-strength mechanical properties specified in Table S24.1 with little danger of cracking or distortion. 1.3 The material is not intended for use in the solution heat-treated condition. NOTE 1—If the service environment in which the material is to be used is considered conducive to stress-corrosion cracking, precipitation hardening should be performed at a temperature that will minimize the susceptibility of the material to this type of attack. 1.4 Supplementary requirements of an optional nature are provided for use at the option of the purchaser. The supplementary requirements shall apply only when specified individually by the purchaser in the purchase order or contract. 1.5 This specification is expressed in both inch-pound units and in SI units; however, unless the purchase order or contract specifies the applicable M-specification designation (SI units), the inch-pound units shall apply. 1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard. 1.6.1 Within the text, the SI units are shown in brackets. 1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
ASTM A747/A747M-18 Referenced Document
- ASTM A1067/A1067M Standard Specification for Test Coupons for Steel Castings*， 2024-04-20 Update
- ASTM A1080 Standard Practice for Hot Isostatic Pressing of Steel, Stainless Steel, and Related Alloy Castings*， 2024-04-20 Update
- ASTM A781/A781M Standard Specification for Castings, Steel and Alloy, Common Requirements, for General Industrial Use*， 2021-05-01 Update
- ASTM A957/A957M Standard Specification for Investment Castings, Steel and Alloy, Common Requirements, for General Industrial Use*， 2024-04-20 Update
ASTM A747/A747M-18 history
- 1970 ASTM A747/A747M-23 Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- 2018 ASTM A747/A747M-18 Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- 2016 ASTM A747/A747M-16a Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- 2016 ASTM A747/A747M-16 Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- 2012 ASTM A747/A747M-12 Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- 2007 ASTM A747/A747M-07 Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- 2004 ASTM A747/A747M-04 Standard Specification for Steel Castings, Stainless, Precipitation Hardening
- 1999 ASTM A747/A747M-99 Standard Specification for Steel Castings, Stainless, Precipitation Hardening